Effect of Mechanical Alloying on Structural and Electrical Properties of (P<sub>2</sub>O<sub>5</sub>)<sub>(x)</sub>-(Y<sub>2</sub>O<sub>3</sub>)<sub>(0.03)</sub>-(ZrO<sub>2</sub>)<sub>(0.97)</sub> Electrolyte

Abstract

Pentavalent phosphorous oxide doped yttria-stabilized zirconia (P2O5)X-(Y2O3)0.03-(ZrO2)0.97 with x=0.06 mol.% was achieved via an economical technique using mechanical alloying (MA) technique. Three types of nanocomposite powders of electrolyte were produced by high-energy ball milling with different milling times. The phases of synthesized electrolyte powders and sintered electrolytes were illustrated by X-ray diffraction (XRD). The average particle sizes of powders indicated around (360, 245, and 48) nm at milling duration (1, 10, and 45) hrs, respectively. The XRD analysis results of 1 h MA electrolyte powder obtained tetragonal ZrO2, while the 45 h MA electrolyte manifested a minority phase of monoclinic ZrO2. Then, the XRD of the sintered electrolyte with the optimum electrical properties appeared two phases. The major phase of the tetragonal zirconium yttrium oxide and a minor phase was a monoclinic zirconium oxide. The average grain sizes of the three types of the sintered manufacturing electrolytes were (7.638, 2.642, and 1.245 µm) after the mechanical alloying duration of (1, 10, and 45) hrs, respectively and sintered at 1873 °K. The DC conductivity (σ) studied corresponded to the influence of milling times on the microstructure for each sintered electrolyte. From the results, the synthesized sintered electrolyte with a long MA duration gave a maximum DC (σ) 1.03E-1S.m. And, the DC conductivity (σ) was 1.11E-02 of electrolyte produced with 10 hr mechanical alloying. Otherwise, the lower DC conductivity got with the electrolyte prepared in the lowest milling duration was 8.9 E-2 S.m.