Acoustic emission (AE) measurement has been used to investigate microscopic failures and damage progress in carbon fiber reinforced plastics (CFRP). In this work, AE measurements were conducted on plain-woven CFRPs fabricated by vacuum-assisted resin transfer molding process and neat epoxy resins during tensile tests to evaluate the failure modes. Four types of epoxy resins were used as matrix resins to investigate the effects of matrix resin characteristics on the microscopic damage behavior and the mechanical properties of CFRP. As a result, the mechanical properties of on-axis CFRP were comparable regardless of matrix resins. On the other hand, in the case of off-axis CFRP, such as 45° direction, the tensile strength was remarkably lower with a brittle matrix resin. From the AE measurement results, the number of cumulative hits for CFRP was much larger than that for neat resins due to the occurrence of fiber/matrix interfacial cracks. Also, AE waves for CFRP had a longer duration than that for neat resin, and the relationship between the degree of duration and fracture mode was clarified.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.