Abstract
The effect of magnesium addition on the number, morphology, composition, size, and density of inclusions in H13 die steel was studied. The results show that the total oxygen content in the steel can be significantly decreased to 0.0008wt%. Al2O3 and MnS inclusions are changed into nearly spherical MgO·Al2O3 spinel and spherical MgO·MgS inclusions, respectively. The number of inclusions larger than 1 μm decreases and the number of inclusions smaller than 1 μm increases with increasing magnesium content. V(N,C) precipitates around MgO·Al2O3 and MgO·MgS inclusions during solidification of liquid steel. The densities of MgO·Al2O3 spinel inclusions are lower than that of alumina inclusions. With increasing magnesium content in the Mg-containing inclusions, the density of inclusions decreases, leading to the improvement of inclusion removal efficiency.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: International Journal of Minerals, Metallurgy, and Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.