Effect of local cooling rates on the microstructures of single crystal CMSX-6 superalloy: A comparative assessment of the Bridgman and the downward directional solidification processes

Abstract

Single-crystal nickel-based CMSX-6 superalloy rods were directionally solidified at a constant withdrawal rate by employing a novel directional solidification process—the downward directional solidification process and the Bridgman process. For the rods cast using both processes, the local cooling rates were measured at the 5.5cm and 12.5cm locations between the solidification front and the chill end. With an increasing distance from the chill, the cooling rate varied from 1.21 to 1.08K/s giving a change in the rate of 10.74% in the novel process. In contrast to this, the cooling rates in the Bridgman process varied from 0.15 to 0.08K/s giving a change in the rate of 46.67%. The microstructural evolution was comparatively investigated for the two processes as a function of the cooling rates. In comparison to the Bridgman process, refined γ dendrite structures, smaller size of γ/γ′ eutectic island, refined γ′ precipitates in the dendritic core and a smaller average size of microporosities were observed in both locations of the rods cast by using the novel process. In addition to this, the variations of the primary and secondary dendrite arm spacings, the size of γ/γ′ eutectic island, and the size of γ′ precipitates in the dendrite core were smaller than those in the Bridgman process with increasing the distance from 5.5cm to 12.5cm. This indicates that the downward directional solidification process can cast a rod possessing more homogeneous microstructures. Moreover in comparison to the Bridgman process, the majority of the micropores have smaller diameters and both the variation in the maximum size of microporosity as well as the average diameter of these micropores located between positions near to the chill end and the distant end were smaller in the rods cast by using the novel process; the opposite is found in the Bridgman process.