Abstract
The microstructure of LiNi0.8Co0.1Mn0.1O2 cathode materials was controlled by the addition of lithium silicate, and the influence on the cycle performance and the rate capability was investigated. Si was not included within the lattice, but localized at the grain boundaries of the primary particles and the pores inside the secondary particles. The addition of the lithium silicate greatly decreased the density of the pores between the primary particles and improved the density of the secondary particles. The capacity retention was successfully improved for lithium silicate-added LiNi0.8Co0.1Mn0.1O2. When lithium silicate-free LiNi0.8Co0.1Mn0.1O2 was charged to 4.3 V, many cracks were formed along the grain boundaries even in the first cycle, while crack formation was remarkably inhibited for lithium silicate-added LiNi0.8Co0.1Mn0.1O2. Moreover, lithium silicate-added LiNi0.8Co0.1Mn0.1O2 particles were almost free from visible microcracks even after 100 cycles at the discharged state. These results suggest that the lithium silicate reinforces the grain-adhesion at the grain boundaries, inhibiting crack formation and electrolyte decomposition inside the cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.