Alumina specimens with small amounts of CaO and TiO2 were prepared and their microstructural evolution during sintering was investigated. Because of the appearance of a liquid phase during sintering, a duplex microstructure of a few abnormal grains and fine matrix grains was obtained when the CaO + TiO2 content was small (≤0.04 wt%). When the CaO + TiO2 content was relatively high (≥0.1 wt%), many grains grew and impinged upon each other. As a result, a rather uniform and homogeneous microstructure was observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.