Abstract
A two powder process was used to prepare silver-sheathed monofilamentary Bi{sub 1.8}Pb{sub x}Sr{sub 1.98}Ca{sub 1.97}Cu{sub 3.08}O{sub y} (Bi-2223) tapes with varying lead contents, x, from 0.2 to 0.5. The resulting tapes were subjected to thermomechanical processing and then characterized by x-ray diffraction (XRD), scanning electron microscopy (SEM), and energy dispersive x-ray analysis (EDX). Layered phase texture was accessed using image analysis software on scanned SEM micrographs. Transport currents were measured at 77 K and zero field by the four-probe method. It was found that tapes with low lead content (X = 0.2 and 0.25) showed incomplete conversion to Bi-2223, had small grain size and poor c-axis texture. Tapes having higher lead content (x = 0.4 and 0.5) also showed incomplete conversion and the presence of lead-rich secondary phases. Tapes with lead content x = 0.3 and 0.35 showed complete conversion to Bi-2223, and had the least amount of secondary phases, the best c-axis texture, and the highest transport current (j{sub c}). The carbon content of the precursor powder also had a strong influence on secondary-phase chemistry.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.