Effect of layering strategy and prolonged water aging on masking ability of composite resins

Abstract

Statement of problemLayered composite resins may adequately mask discolored substrates. However, whether color changes that occur over time affect masking ability is unclear. PurposeThe purpose of this in vitro study was to investigate the effect of layering and water aging on the masking ability of 2 composite resins. Material and methodsDisk specimens (1.5 mm-thick and shade A1) from Charisma Diamond (CD) and Filtek Z350XT (Z350) were made according to the composite resin shade combination used in the layering strategies: bilayer for CD (enamel/dentin) and for Z350 (enamel/body and enamel/dentin) and trilayer for Z350 (enamel/body/dentin) (n=5). Color measurements were obtained with a spectrophotometer over an A3.5 ceramic substrate, and the whiteness index for dentistry (WID) was calculated. The specimens were aged in water at 37 °C and evaluated at different times: 24 hours, 1 week, 1 month, 2 months, 6 months, 12 months, 18 months, and 24 months. CIEDE2000 color differences (ΔE00) and WID differences (ΔWID) were calculated and interpreted by 50:50% color and whiteness perceptibility and acceptability thresholds. Changes among strategies and aging times were analyzed using the Kruskal-Wallis test (α=.05). Contrasts were made using the Mann-Whitney U test with Bonferroni correction (α=.001). ResultsΔE00 decreased from 24 hours to 2 months of aging. From 2 months onwards, ΔE00 increased for all layering strategies and times, without significant changes in lightness for CD (P>.004). Overall, for the CD restorative system, an increase in ΔWID was observed after 1 month of aging (P<.001), while for the Z350 restorative system, ΔWID decreased after aging (P<.001), except for the Z350 bilayer strategy (enamel + dentin) at 1 week and 2 months (P>.004). For all layering strategies and aging times, color differences were higher than the 50:50% perceptibility threshold for ΔE00 and, after 6 months, higher than the 50:50% acceptability threshold for ΔE00 and the 50:50% whiteness acceptability threshold. ConclusionsThe ability of the tested composite resins to mask a discolored substrate was affected by the layering approach applied and by prolonged water aging.