Abstract
The influence of laminate thickness of polymer matrix composites on moisture diffusion in seawater immersion, as well as the resulting mechanical property degradation for composites of glass/isopolyester (G/IPE), carbon/isopolyester (C/IPE), glass/vinylester (G/VE) and carbon/vinylester (C/VE), was investigated in this paper. Laminates 3 and 10mm in thickness, fabricated using the wet hand lay-up technique, were characterized for moisture absorption in artificial seawater medium, and their flexural strength and interlaminar shear strength (ILSS) degradations were studied. Moisture diffusion was observed to be anamolous to the Fick’s law for both 3 and 10mm thick samples in the later stage of diffusion. Moisture permeability of 10mmthick samples was two to three order greater than that of 3mm thick ones, while the time to moisture saturation remained unchanged. With the increase of laminate thickness, moisture saturation increased by 1.4% for C/VE and 7% for G/IPE. The residual flexural strength and ILSS were greater in case of 10mm thick specimens after 200 days of exposure. SEM examination of the fractured specimens showed greater levels of fibre/matrix debonding in 10mm thick specimens.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.