Abstract
The effect of La2O3 addition on the microstructure and electrical properties of Mn0.75Ni1.25CuO4-xLa2O3 (0≤x≤0.3) was studied. The crystal structure, phase compositions and morphology were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy-dispersive spectroscopy (EDS). The sintered ceramic bodies was typical polycrystalline, with cubic spinel structure of copper manganese oxide, rocksalt structure of nickel copper oxide, along with monoclinic phase of copper oxide and orthorhombic perovskite structure of lanthanum manganese oxide. The obtained ρ77K, B77K/90K constant and activation energy of the thermistors were in the range of 3.88-9.29 Ω cm, 245-261 K, and 0.0211–0.0225 eV, respectively. This means that the electrical properties can be adjusted to desired values, depending on the La content. So these prepared thermistors were intended to be used under low temperature conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.