Abstract
ABSTRACTThe effect of mixed rare earth (La+ Yb) addition on the fluidity of A356.2 was investigated by fluidity tests, optical microscope (OM), environmental scanning electron microscope (ESEM) with energy diffraction spectrum (EDS) and X-ray diffraction (XRD). Varying amounts of (La+ Yb) addition were tested, 0%,0.3%,0.6%, and 0.9% (wt.%). The fluidity of A356.2 was improved with the addition of mixed rare earth (La+ Yb). The fluidity length of the A356.2 + 0.6% (La+ Yb) alloy (670mm) was increased by 19% compared to that of A356.2 (565mm). The fluidity of the alloy was related to the morphology of α-Al and Al8Si6Mg3Fe(Fe phase)in the alloy. A refined microstructure of the alloy corresponded with better fluidity. A higher pouring temperature also improved fluidity. However, this trend declined when the pouring temperature increased above 730°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.