Abstract
The effect of La substitution on the structural and electrical properties of multiferroic BiFeO3 thin films grown on Pt∕TiO2∕SiO2∕Si substrates by pulsed laser deposition has been reported. X-ray diffraction data confirmed the substitutions of La into the Bi site with the elimination of all of the secondary phases. The dielectric constant of the films was systematically increased from 165 to ∼350 and the films showed excellent dielectric loss behavior. We observed a gradual increase in the remnant polarization (2Pr) with lanthanum substitution obtaining a maximum value of ∼42μC∕cm2 at 20mol% La incorporation. The leakage current behavior at room temperature of the films was studied and it was found that the leakage current decreased from 10−4to10−7A∕cm2 for La-substituted films at a field strength of 50kV∕cm. The reduction of dc leakage current of La-substituted films is explained on the basis of relative phase stability and improved microstructure of the material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.