Abstract
Semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys were prepared by semi-solid isothermal heat treatment. The effects of the La element on the as-cast and semi-solid microstructures of Mg-7Zn alloy were investigated. Meanwhile, the effects of isothermal temperature and holding time on the evolution of the semi-solid microstructure of Mg-7Zn-0.3La alloy were also studied. Results indicate that the addition of a small amount of La can significantly refine the as-cast and semi-solid microstructure. During the semi-solid thermal transformation, the size and shape factor of solid particles decrease at first and then increase with the increase of isothermal temperature and holding time. The semi-solid microstructure of Mg-7Zn-0.3La alloy obtained by holding at 605 °C for 30 min is the optimal. The average size of solid particles, shape factor, and solid fraction are 42 µm, 1.45 and 61.8%, respectively. At the same time, a comparative study on the coarsening process of particles in the semi-solid billets of Mg-7Zn and Mg-7Zn-0.3La alloys reveals that the addition of La effectively decreases the coarsening rate of solid particles and restricts the growth of solid particles.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.