Abstract
This study discusses the effect of kaolin/PESf ratio and sintering temperature on the pore size and porosity of the flat sheet kaolin membrane support. Inexpensive kaolin has been proposed as a replacement for A12O3, Ti2O and ZrO2 as a membrane material. In casting the support precursor, Polyethersulfone (PESf), solvent N-methyl-2-pyrrolidone (NMP) and kaolin were used as a polymer binder, solvent and ceramic powder, respectively. The morphology structure and pore size were observed under the Scanning Electron Microscope (SEM) and the porosity were obtained by calculation using weight loss, area and thickness data of the prepared support. The results showed that both of the membrane pore size and porosity linearly decreased from 20 to 8 I¼m and 26 to 11%, respectively when sintering temperature was increased from 1100 to 1500°C and kaolin/PESf ratio was increased from 1:1 to 3.5:1.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.