Abstract
Ti–5Al–5V–5Mo–3Cr (Ti-5553) sheets were welded using a Nd: YAG laser system and Ti–6Al–4V filler wire. The effect of joint gap on weld geometry, defects, microstructure, and hardness was investigated. Fully penetrated welds up to a joint gap of 0.5 mm were produced. The two main defects observed were porosity and underfill. The addition of filler wire reduced underfill but increased porosity, especially at large joint gaps. The fusion zone (FZ) microstructure at low joint gaps consisted of retained β with a dendritic morphology. At a joint gap of 0.3 mm, regions of orthorhombic α″ martensite were observed in the weld zone which increased in proportion as the joint gap increased from a volume percentage of 4.9% at 0.3 mm to a volume percentage of 44% at 0.5 mm. Despite the differences in microstructure with increasing joint gap, the FZ hardness remained relatively constant for all joint gaps evaluated.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.