Abstract

The combined effects on long-term reliability of isothermal aging and chemically balanced or unbalanced surface finish have been investigated for fine-pitch ball grid array packages with Sn–3.0Ag–0.5Cu (SAC305) (wt.%) and Sn–3.5Ag (SnAg) (wt.%) solder ball interconnects. Two different printed circuit board surface finishes were selected to compare the effects of chemically balanced and unbalanced structure interconnects with and without board-side Ni surface finish. NiAu/solder/Cu and NiAu/solder/NiAu interconnects were isothermally aged and thermally cycled to evaluate long-term thermal fatigue reliability. Weibull plots of the combined effects of each aging condition and each surface finish revealed lifetime for NiAu/SAC305/Cu was reduced by approximately 40% by aging at 150°C; less degradation was observed for NiAu/SAC305/NiAu. Further reduction of characteristic life-cycle number was observed for NiAu/SnAg/NiAu joints. Microstructure was studied, focusing on its evolution near the board and package-side interfaces. Different mechanisms of aging were apparent under the different joint configurations. Their effects on the fatigue life of solder joints are discussed.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.