Abstract
The effect of the support nature on the catalytic activity of platinum and ruthenium nanoparticles is investigated for ethylene complete oxidation in the temperature range of 25–220°C. The nanoparticles (NPs) were deposited on ionically conductive supports: yttria-stabilized zirconia (YSZ) and samarium-doped ceria (SDC), and on non-ionically conductive supports: carbon black (C) and gamma-alumina (γ-Al2O3) to give ≤0.7wt% loading and an average particle sizes of 1.9–2.9nm depending on the support. The presence of O2− ionic conductivity greatly enhanced Pt and Ru catalytic activity compared with the same metals deposited on non-ionically conductive supports for C2H4 complete oxidation. The light off temperatures of Pt/SDC and Ru/SDC were 60°C and 70°C, respectively, whereas for the same NPs deposited on the high surface area carbon, the higher temperatures of 90°C for Pt/C and 130°C for Ru/C were obtained. The same trend was observed with activation energies, which were 22 and 35.1kJ/mol for Pt/SDC and Ru/SDC compared with 31 and 52.4kJ/mol for Pt/C and Ru/C, respectively. It is proposed that metal–support interaction (MSI), in particular, the electronic effect between NPs and ionic conductors is responsible for the high catalytic activity. The electronic effect is manifested by the oxygen ion exchange in the vicinity of the three-phase boundary similar to the electrochemical promotion mechanism, which is thermally self-induced in the case of Pt and Ru NPs deposited on SDC and YSZ.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.