Abstract
Abstract. This paper investigated the Cf/SiC ceramic matrix composites. By utilizing different interfacial treatment processes to prepare carbon-fiber preform, the preform was then densified by infiltration and pyrolysis(PIP) with polycarbosilan/xylene solution as precursor, and the Cf/SiC ceramic matrix composite specimens were fabricated. Mechanical tests such as bending test and fracture toughness were performed for Cf/SiC samples. The results show that the interfacial bonding strength in the sample with high-temperature treatment process was improved due to removing surface sizing. The samples which were treated up to 1400°C exhibited the highest three-point flexural strength, up to 595MPa; The samples which were treated up to 1400°C and deposited by pyrolytic carbon(PyC) coating shows the highest fracture toughness value which was 20.70MPa•m1/2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.