Abstract
The purpose of this study is to improve the properties of the feedstocks and shape retention of debinded parts by the reaction between 17-4PH stainless steel powders. Carboxyl-terminated hyperbranched polyester (CTHP) and epoxy-terminated hyperbranched polyester (ETHP) were used to treat the powders, and termed as CTHP-m and ETHP-m with carboxyl and epoxy group, respectively. Comparing with pristine, CTHP-m and ETHP-m, feedstock prepared from equal amount of CTHP-m and ETHP-m (CTHP-m/ETHP-m) possessed more excellent properties. The experimental results showed that the critical solids loading, flexural modulus, density and melt flow index of CTHP-m/ETHP-m feedstock were 63.8 vol.%, 2800 Mpa, 5.06 g cm−3 and 62 g/10 min, respectively, which were obviously higher than that of others. Also, the shape retention of CTHP-m/ETHP-m debinded parts was the best of all the samples. The improved properties of CTHP-m/ETHP-m feedstock were attributed to the powder interaction between CTHP-m and ETHP-m formed by the chemical reaction between epoxy and carboxyl group.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.