Abstract
Interaction between the intrinsic (native) defects and the irradiation-induced defects created by neutron irradiation was examined for the YBCO sample. For this purpose, non-superconducting Y-211 phase was included to the Y-123 samples at different contents as a source of large pinning center. The critical current density enhancement with the irradiation for these samples were analysed and then the role of defects on pinning improvement was discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.