Abstract

The effect of initial grain size on the recrystallization behaviour of a type 304 austenitic stainless steel was investigated using hot torsion. Refinement of the initial grain size to 8 μm had a considerable effect on the flow curve shapes, peak and critical strains and also on DRX kinetics, compared with an initial grain size of 35 μm. Microstructural investigations using EBSD suggest a transition from conventional (discontinuous) to continuous dynamic recrystallization with decreasing initial grain size. Also, there was a moderate effect of initial grain size on the DRX grain size.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.