Abstract
This paper presents the effect of indium (In) content on the melting temperature, wettabililty, dross formation, and oxidation characteristics of the Sn-2Ag-3Bi-xIn alloy. The melting temperature of the Sn-2Ag-3Bi-xIn alloy (2 ≤ x ≤ 6) was lower than 473 K. The melting range between the solidus and liquidus temperatures was approximately 20 K, irrespective of the indium content. As the indium content increased, the wetting time increased slightly and the maximum wetting force remained to be mostly constant. The dross formation decreased to approximately 50% when adding 1In to Sn-2Ag-3Bi, and no dross formation was observed in the case of Sn-2Ag-3Bi-xIn alloy (x ≥ 1.5) at 523 K for 180 min. Upon approaching the inside of the oxidized solder of the Sn-2Ag-3Bi-1.5In alloy from the surface, the O and In contents decreased and the Sn content increased based on depth profiling analysis using Auger electron spectroscopy (AES). The mechanism for restraining dross (Sn oxidation) of Sn-2Ag-3Bi alloy with addition of indium may be due to surface segregation of indium. This is due to the lower formation energy of indium oxide than those of Sn oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.