Abstract
This study investigated the effect of immersion in sodium hypochlorite (NaOCl) on torque and fatigue resistance of two nickel-titanium files. Size 25 .04 ProFile and RaCe files were immersed in 5.25% NaOCl for 1 or 2 hours at temperatures of 21 degrees C and 60 degrees C. Torque and angle at failure were measured according to ISO 3630-1. Resistance to cyclic fatigue was determined by counting rotations to breakage in a 90 degrees curve with a 5-mm radius. Data were analyzed by 2-way analysis of variance. Torsional resistance of both rotaries was not significantly affected by immersion in NaOCl, except after 2 hours of immersion at 60 degrees C. Resistance to cyclic fatigue decreased significantly for ProFile and RaCe instruments after immersion in NaOCl. Spontaneous fractures occurred in 28 of 160 files during immersion in NaOCl. In conclusion, nickel-titanium rotaries have reduced resistance to cyclic fatigue after contact with heated NaOCl and may then be considered single-use instruments.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Journal of Endodontics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.