Abstract
Hydroxyapatite (HAp) microcrystals were synthesized by a neutralization reaction of Ca(OH)2 suspension and H3PO4 solution using an ultrasonic homogenizer. The in vitro interaction of HAp microcrystals with rat peritoneal macrophages was investigated by measuring the viability, acid phosphatase (ACP) activity, lactate dehydrogenase (LDH) activity and intracellular calcium content. HAp calcined at 800 degrees C and alpha-alumina particles (alumina) were used as comparative materials. Macrophages actively phagocytosed HAp microcrystals by dissolving them. However, no damage in macrophages exposed to HAp microcrystals was observed by transmission electron microscopy. Macrophages in the presence of HAp microcrystals showed less ACP and LDH activity and higher intracellular calcium content than those in the presence of calcined HAp and alumina. HAp microcrystals had excellent biocompatibility to macrophages as well as sintered HAp.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.