Abstract
The hydride phase in the Ti-5.6Al-4.8Sn-2.0Zr alloy after hydrogenation was investigated through TEM and XRD analysis. The experimental results show that the phase transition temperature of the hydrogenated Ti-5.6Al-4.8Sn-2.0Zr alloy is decreased approximately by 150–200°C. XRD analysis verifies that the hydrogenation treatment accelerates the phase transition process from α phase to β phase of the Ti-5.6Al-4.8Sn-2.0Zr alloy, so as to decrease the phase transition temperature of the alloy. Meanwhile, TiH2 hydride (δ phase) with strip structure appears in α phase and β phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.