Abstract
The effects of hydrogen on the tensile properties, fatigue life, and tensile and fatigue fracture morphologies of nitrogen-added ultrahigh-strength transformation-induced plasticity (TRIP)-aided martensitic (TM) steels were investigated. The total elongation and number of cycles to failure (Nf) of the hydrogen-charged TM steels decreased with the addition of nitrogen; in particular, adding 100 ppm of nitrogen decreased the total elongation and Nf of the TM steels. The quasi-cleavage cracking around the AlN occurred near the sample surface, which is the crack propagation region, although dimples appeared at the center of the fracture surface in the tensile samples. The initial fatigue crack initiated at the AlN precipitate or matrix/AlN interface, located at the notch root. During crack propagation, new cracks were initiated at the AlN precipitates or matrix/AlN interfaces, while quasi-cleavage crack regions were observed around the AlN precipitates. The decrease in the total elongation and Nf of the hydrogen-charged TM steel with 100 ppm of added nitrogen might be attributable to the crack initiation around the AlN precipitates formed by a large amount of hydrogen trapped at the AlN precipitates and matrix/AlN interfaces, and to the dense distribution of AlN, which promoted crack linkage.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.