Abstract
Hydrogen absorption leads to redistribution of the components of the surface layer of the amorphous alloy Fe73.8Si12.7B9.4Nb3.2Cu noncontact side, while the amorphous structure of this layer is preserved. The type of the micro-groups Fey Six changes in such a way that the ratio y: x decreases (to less than 1) and the chemical bond polarity decreases, as well. After degassing, the surface layer composition becomes similar to those before hydrogenation. The loss of the mechanical stability of the amorphous ribbon is accompanied by the formation of the micro-groups Fey Six with a decreased ratio of y: x.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.