Abstract
Objectives. Micromechanical retention from the hybrid layer is generally believed to be the mechanism of adhesion of current generation dentin bonding agents. The purpose of this investigation is to evaluate the interfacial fracture toughness of a commercial dentin bonding agent with and without this hybrid layer. Methods. Ten extracted molars (AB2) were flattened on the occlusal surface, All-Bond 2 Universal Adhesive System (Bisco) was applied according to manufacturer's directions and a composite resin (Prodigy, Kerr) crown was formed. Another group of ten molars (AB2Cl) was handled identically with the exception of a 1 min gentle scrubbing application of 5.25% sodium hypochlorite after acid etching to remove the acid-exposed collagen. Plane-strain chevron-notch short bar fracture toughness specimens were fabricated from all 20 composite crowns and tested according to ASTM E1304-89. Each group was tested to failure in tensile mode at 0.1 mm min −1 and the maximum load at failure was used to determine plane-strain fracture toughness ( K QvM). Weibull parameters were calculated and fracture probability distributions were tested for significant difference at the 95% confidence level. Scanning electron microscopy was employed on broken specimens (18/20) to describe the failure mode. Results. Weibull distributions were not significantly different with characteristic plane-strain fracture toughness from maximum load ( K o QvM) of 0.97 MPa m 1/2and 0.81 MPa m 1/2 and a Weibull modulus of 4.7 and 3.9, respectively, for AB2 and AB2Cl. All AB2 samples failed within the adhesive joint, while the AB2Cl crack propagated from the interphase of adhesive resin and dentin to 1–2 μm into dentin. Significance. Under the conditions of this study, the presence of collagen did not contribute to a significantly stronger bonded joint. Interfacial fracture toughness evaluation of the dentin–composite resin bimaterial interface shows promise for future investigations.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.