Abstract
The Zn-rich Al-11.3Zn-2.65Mg-1Cu alloy was prepared by spray forming rapid solidification technology and then processed by hot extrusion and heat treatment to T6-temper condition. The characteristics of spray-formed and extruded materials are systematically investigated, and accordingly, solution treatment parameters are derived at an intermediate temperature. The tensile results indicate that the alloy can reach yield strength as high as 807 MPa due to massive precipitation of ή phase which is attributed to the high supersaturation of the solutionized alloy because of the cumulative effect of spray forming and optimal solution treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.