Abstract
The effect of homogenization on the hardness, tensile properties, electrical conductivity and microstructure of as-cast Al-6Mg-0.4Mn-0.25Sc-0.12Zr alloy was studied. The results show that during homogenization as-cast studied alloy has obviously hardening effect that is similar to aging hardening behavior in traditional Al alloys. The precipitates are mainly Al3(Sc,Zr) and Al6Mn. When homogenization temperature increases the hardness peak value is declined and the time corresponding to hardness peak value is shortened. The electrical conductivity of the alloy monotonously increases with increasing homogenization temperature and time. The decomposition of the supersaturated solid solution containing Sc and Zr which is formed during direct chilling casting and the precipitation of Al3(Sc, Zr) cause hardness increasing. The depletion of the matrix solid solubility decreases the ability of electron scattering in the alloy, resulting in the electrical conductivity increased. Tensile property result at hot rolling state shows that the optimal homogenization treatment processing is holding at 300–350 °C for 6–8 h.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.