Abstract
The effect of holding time, thickness and annealing heat treatment on the microstructure and some mechanical properties of compacted graphite iron (CGI) are studied. Samples of CGI are produced in Helwan factory for casting by using GGG 70 as base metal in a medium frequency induction furnace. The mechanical properties (tensile strength, and hardness) of the as-cast and after heat treatment samples are determined and the microstructure of the samples is examined using optical microscope. The results show that the mechanical properties and microstructure of CGI depend on holding time, thickness and annealing heat treatment; it is found that increasing the holding time from 10min to 17min results in lowering the Mg content from 0.031% to 0.021% and as a result lower nodularity was obtained. Lowering the thickness from 20mm to 5mm increases the tendency of dendritic structure as a result of increasing the cooling rate. The annealed samples with mainly ferritic matrix gave the lowest tensile strength and hardness value compared with the as-cast conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.