Abstract
Stainless steels suffer from classical sensitization when encounter at certain temperature which results in precipitation of chromium carbide along grain boundary with simultaneous depletion of chromium from near grain boundaries. This study focused on corrosion potential test at different sensitization condition. The degree of chromium carbide precipitation was measured based on thickness of grain boundary. With increasing holding time, the thickness of the chromium depletion zone also increases due to diffusion of chromium into solid solution. Corrosion potential test showed that the heated sample at 700°C for 60 minutes resulted in highest corrosion current density and shifted its corrosion potential to more active potential. The potential tend to increase with increasing the degree of chromium carbide precipitation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.