Abstract
The microstructure and properties of Cu-TiB2 composites produced by high-energy ball-milling of TiB2 powders and spark-plasma sintering (SPS) were investigated. TiB2 powders were mechanically milled at a rotation speed of 1000rpm for short time in Ar atmosphere, using a planetary ball mill. To produce Cu-xTiB2 composites( x = 2.5, 5, 7.5 and 10wt.% ), the raw and milled TiB2 powders were mixed with Cu powders by means of a turbular mixer, respectively. Sintering of mixed powders was carried out in a SPS facility under vacuum. High-energy ball-milling resulted in refinement of TiB2 particles. XRD patterns of milled TiB2 powders indicated broader TiB2 peaks with decreased intensities. After sintering at 950 for 5min using the raw and milled TiB2 mixture powders, the sintered density decreased with increasing TiB2 content regardless of milling of TiB2. In the case of raw TiB2, hardness rapidly increased from 4 to 44 HRB with increasing TiB2 content. The electrical conductivity changed from 95.5 to 80.7 %IACS. For mixtures of Cu powders with milled TiB2 powders, hardness increased from 38 to 67 HRB as TiB2 content increased, while the electrical conductivity varied from 88% to 51 % IACS. When compared to compacts sintered with raw and milled TiB2 powders, the electrical conductivity of specimens with raw TiB2 powder was higher than that of specimens with milled TiB2 powder, while hardness was slightly lower.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.