Abstract
To investigate the effects of homogenizing and aging treatments on the microstructure of an Nb-Ti-Cr-Si based ultrahigh temperature alloy, coupons were homogenized at 1 200-1 500 °C for 24 h, and then aged at 1 000 °C for 24 h. The results show that the heat-treated alloy is composed of Nb solid solution (Nbss), (Nb,X) 5Si 3 and Cr 2Nb phases. With the increase of heat-treatment temperature, previous Nbss dendrites transformed into equiaxed grains, and petal-like Nbss/(Nb,X) 5Si 3 eutectic colonies gradually changed into small (Nb,X) 5Si 3 particles distributed in Nbss matrix. A drastic change occurred in the morphology of the Laves phase after homogenizing treatment. Previously coarse Cr 2Nb blocks dissolved during homogenizing at temperature above 1 300 °C, and then much finer and crowded Cr 2Nb flakes precipitated in the Nbss matrix in cooling. Aging treatment at 1 000 °C for 24 h led to further precipitation of fine particles of Laves phase in Nbss matrix and made the difference in concentrations of Ti, Hf and Al in Nbss, (Nb,X) 5Si 3 and Cr 2Nb phases reduced.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.