Abstract
Ni60Nb40 metallic glass particles, prepared by mechanical alloying, were used to fabricate Al–30 wt% Ni60Nb40 metal matrix composites (MMCs) at 823 K by sintering, hot pressing, and hot extrusion. The Ni60Nb40 reinforcements remained amorphous in all the MMCs fabricated by the different methods. Compression tests revealed that the Young’s modulus and yield strength of the MMCs produced by hot-pressing and hot-extrusion are higher than those for the sintered specimens. Differential scanning calorimeter (DSC) annealing of the as-produced MMCs at 913 K revealed there are severe interfacial reactions between the Al matrix and the Ni60Nb40 reinforcements. The DSC isotherms indicate that the Al matrix reacts faster with Ni60Nb40 in the hot-pressed and hot-extruded MMCs than it does in the sintered material.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.