Effect of hexagonal boron nitride and calcined petroleum coke on friction and wear behavior of phenolic resin-based friction composites

Abstract

Calcined petroleum coke (CPC) and hexagonal boron nitride (h-BN) were used as the friction modifiers to improve the friction and wear properties of phenolic resin-based friction composites. Thus, the composites with different relative amounts of CPC and h-BN as the friction modifiers were prepared by compression molding. The hardness and bending strength of the friction composites were measured. The friction and wear behaviors of the composites sliding against cast iron at various temperatures were evaluated using a pin-on-disc test rig. The worn surfaces and wear debris of the friction composites were analyzed by means of scanning electron microscopy, energy dispersive spectroscopy, and X-ray photoelectron spectroscopy. It was found that the hybrid of the two friction modifiers was effective to significantly decrease the wear rate and stabilize the friction coefficient of the friction composites at various temperatures by forming a uniform lubricating and/or transferred film on the rubbing surfaces. The uniform and durable transfer films were also able to effectively diminish the direct contact between the friction composite and the cast iron counterpart and hence prevent severe wear of the latter as well. The effectiveness of the hybrid of CPC and h-BN in improving the friction and wear behavior of the phenolic resin-based friction modifiers could be attributed to the complementary action of the “low temperature” lubricity of CPC and the “high temperature” lubricity of h-BN. The optimum ratio of the two friction modifiers CPC and h-BN in the friction composites was suggested to be 1:1, and the corresponding friction composite showed the best friction-reducing and antiwear abilities.