Effect of hemicellulose content on the solution properties of cellulose carbamates in NaOH/ZnO aqueous system

Abstract

Hemicellulose removal from bleached bamboo pulp is key to produce qualified dissolving pulps. In this work, alkali/urea aqueous solution was firstly applied to remove hemicellulose in bleached bamboo pulp (BP). The effect of urea usage, time and temperature on the hemicellulose content of BP was studied. The reduction of hemicellulose content from 15.9 to 5.7 % was achieved in 6 wt% NaOH/1 wt% urea aqueous solution at 40 °C for 30 min. Cellulose carbamates (CCs) were obtained from the esterification of BP with urea. The dissolution behavior of CCs in NaOH/ZnO aqueous solutions with different degree of polymerization (DP), hemicellulose and nitrogen contents were studied by using optical microscope and rheology. The highest solubility was up to 97.7 % when the hemicellulose was 5.7 % and Mη was 6.5 × 104 (g/mol). With the decrease of hemicellulose content from 15.9 % to 8.60 % and 5.70 %, the gel temperature increased from 59.0, 69.0 to 73.4 °C. The apparent gelation time increased from 5640 to 12,120 s with the hemicellulose content increased from 8.60 % to 15.9 %. CC solution with 5.70 % hemicellulose always keeps a liquid-state (G" > G') until the test time reached 17,000 s. The results showed that the removal of hemicellulose, the decrease of DP and the increase of esterification endowed CC with higher solubility and solution stability.