High performance tubular carbon membrane (TCM’s) for CO2 separation were prepared by controlling the carbonization heating rates in range of 1-7 oC/min carbonized at 800 oC under Argon environment. A single permeation apparatus was used to determine the gas permeation properties of the membrane at room temperature. Fine turning of the carbonization condition was necessary to obtain the desired permeation properties. The preparation of PI/NCC-based TCM at low heating rate caused the gas permeance for the examined gas N2 and CO2 decreased whereas the selectivity of CO2/N2 increased. It was also identified that the gas permeation properties of the resultant TCM and its structure was highly affected by the heating rate. The best carbonization heating rate was found at 3oC/min for the fabrication of TCM derived via polymer blending of PI/NCC for CO2/N2 separation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Malaysian Journal of Fundamental and Applied Sciences
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.