In this study, a heat-resistant adhesive was prepared using molybdenum-phenolic (Mo-PF) resin as the matrix and TiB2 particle as the ceramizable filler for bonding Al2O3 ceramic substrates. Firstly, Fourier transform infrared (FTIR) was used to characterize the chemical structure of the Mo-PF. Subsequently, thermo gravimetric analysis (TGA) and shear strength testing were employed to investigate the effects of heat treatment in different atmospheres on the thermal stability and residual bonding properties of the adhesive. To further explore the bonding mechanism of the adhesive after heat treatment in different atmospheres, scanning electron microscopy (SEM), compressive strength testing, and X-ray diffraction (XRD) were utilized to analyze the microstructure, mechanical strength, and composition evolution of the adhesive at different temperatures. The bonding strength of Al2O3 joints showed a trend of initially decreasing and then increasing after different temperature heat treatment in air, with the shear strength reaching a maximum value of 25.68 MPa after treatment at 1200 °C. And the bonding strength of Al2O3 joints decreased slowly with the increase of temperature in nitrogen. In air, the ceramicization reaction at a high temperature enabled the mechanical strength of the adhesive to rise despite the continuous pyrolysis of the resin. However, the TiB2 filler in nitrogen did not react, and the properties of the adhesive showed a decreasing tendency with the pyrolysis of the resin.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.