Abstract
This research is aimed to study effect of holding time and temperature in solution treatment and ageing on the hardness of the Aluminum A356 reinforced with silicon carbide particles. Alumimium matrix coposite was particulated with 15 microns-SiC with the content of 15 percent by weight. A356/SiC composites was prepared by the stirr casting. The stirrer was continuously stired at a speed of 300 rpm during acooling temperature to semi-solid state of 610 °C. During stirring the SiC powder was slowly added into the melt and continuously stirred for another 10 min. Then poured into the mold at the pouring temperature of 680°C. A356/SiC composites then subjected to a solid solution treatment with temperature of 540 °C for 1 hr. quenched with water and age hardening temperature of 120 and 135 °C for 3, 6, 12 and 18 hr. The result showed that, in as cast conditions, the composite with 15 microns silicon carbide, the 15 wt%SiC specimen exhibited the average hardness of 64.33 HB. After solution treated, the hardness of samples decreased. the specimen exhibited the average hardness of 53.83 HB. After ageing, the hardness of samples increased. the specimen ageing 120 °C 6 hr. exhibited the lowest average hardness of 51.45 HB while the specimen ageing 135 °C 18 hr. exhibited the highest average hardness of 73.54 HB.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.