Abstract
Ferritic/martensitic (F/M) steels have been recommended as one of the candidate materials for supercritical water cooled reactor (SCWR) in-core components use for its high thermal conductivity, low thermal expansion coefficient and inherently good dimensional stability under irradiation condition in comparison to austenitic steel. CNS-II F/M steel which has good mechanical properties was one of the 9-12Cr F/M steels designed for SCWR in the previous work. In this study a modified CNS-II F/M steel was used and it's ultimate tensile strength was 925 MPa at room temperature and 483 MPa at 600 °C after optimizing heat treatment parameter. The ductile to brittle transition temperature of modified CNS-II F/M steel is −55 °C. Those are at the same level or even higher than that of CNS-II and some commercial F/M steels nominated for SCWR in-core component use. The transmission electron microscope (TEM) results showed that the mechanical properties of the tempered martensite was closely related to the decomposition stage of the martensite.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.