Abstract
AbstractHeat treatments are commonly applied in the martensitic stainless steels to achieve high wear resistance and hardness; however, they can lead to a decrease in corrosion resistance due to the precipitation of chromium‐rich carbides. The present work investigates the effect of austenitizing and tempering parameters on the microstructure, hardness, and passivation and reactivation currents of AISI 440C. A double‐loop electrochemical potentiodynamic reactivation test is performed to evaluate the dissolution and precipitation of chromium‐rich carbides. The volume fraction of phases after heat treatment is estimated by X‐ray diffraction. Results show that an increase in the austenitizing temperature leads to an increase in the carbide dissolution, and also in the amount of retained austenite. As a consequence, low passivation and reactivation currents are obtained. When austenite is the main phase, the increase of austenitizing time contributed to an increase in the degree of sensitization due to austenite grain boundary carbon enrichment. However, the presence of austenite after tempering kept part of the carbon in a solid solution resulting in low passivation and reactivation currents.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.