Abstract
The effect of heat treatment on phase transformation, precipitation behavior and micro-hardness response of Cu40Zn-1.0Ti brass was investigated via powder metallurgy method. The volume fraction of α phase increased with elevated temperature, equaled to that of β phase at 400 °C, and reached to a maximum value of 55.9% at 500 °C. The solid solubility of Ti in Cu40Zn brass matrix decreased with elevated heat treatment temperature, showed high chemical potential for precipitates reaction in Cu40Zn brass. The micro-hardness of the BS40-1.0Ti brass was primarily dependent on the solid solubility of Ti, but also dependent on the phase ratio of α and β phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.