Abstract
The effect of heat treatment at 773 K for 48 h on microstructure and mechanical properties of as-cast Mg 94 Zn 2 Y 4 (at%) alloy was investigated. The results show that block shaped and laths structured 18R long period stacking ordered (LPSO) phase forms directly from the melt. After heat treatment, vast majority of the block shaped and laths structured LPSO phase changes into fine lamellar or needle-like shaped 14H. During heat treatment, a great fraction of LPSO phase is transformed from 18R structure to 14H type. 18R and 14H can co-exist within the α -Mg matrix after solution treatment. As a result, grain sizes are refined to 14∼24 μm (the average grain size is about 19 μm). The co-existence of the block shaped and laths structured phase and needle-like shaped phase help to improve the ultimate tensile strength, yield strength and elongation from 182 MPa, 135 MPa and 10.2% in as-cast alloy to 245 MPa, 157 MPa and 13.8%, respectively
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.