Abstract
AbstractThe effect of tempering treatments on the microstructure and creep behaviour of multipass 1·25Cr–0·5Mo steel weldments has been evaluated. While tempering invariably reduced the hardness, significant changes in microstructure were only found after heat treatment at 750°C. In this case ferrite bands developed adjacent to the fusion boundary. Tempering increased creep deformation and reduced failure lifetime for base metal specimens. For crossweld testpieces, the susceptibility to low ductility failures in the heat affected zone was found to be linked to the development of creep cavities and cracks. Thus, brittle failure modes were a function of stress, temperature, microstructure, post weld heat treatment, and to a lesser extent, specimen geometry.MST/3069
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.