Abstract
Ti-45.5Al-2Cr-4Nb-0.4B alloy was cast by vacuum arc melting at high purity Ar atmosphere using high purity sponge Ti, granular Al (99.99%), flake Nb (99.9%), lump Cr (99.9%) and TiB2 (99.5%) and subsequently heat-treated to obtain a couple of microstructures, i.e. lamellar and near γ. The heat treatment consisted of annealing at a high temperature (1200 ~ 1330oC) of different phase fields for 24 hrs and stabilizing at 900oC for 4 hrs followed by air cooling. Fracture toughness was measured on the specimens with different microstructures at room temperature. The value of KQ of specimen with fully lamella structure was obtained as 18.68 MPa √m, much higher than that of specimen with near γ structure (11.84 MPa √m). It was also revealed that the KQ value was decreased as the annealing temperature decreased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.