Abstract
ABSTRACTA series of epitaxial single crystal ZnO samples were grown by Pulsed Laser Deposition (PLD) on c-axis, double-side polished sapphire at temperatures ranging from 600°C to 800°C. A comprehensive optical study, consisting of cathodoluminescence (CL) and transmission spectroscopy measurements, was performed before and after annealing the samples in air and oxygen environments. The structural characteristics of the films were observed by x-ray diffraction and transmission electron microscopy (TEM). Using these measurements, the data revealed that annealing significantly improved the luminescence and exciton line-width of the better material grown at the higher end of the temperature range. In lower quality samples grown at the lower end of the temperature range, the optical quality of the material was degraded. In the samples grown at higher temperatures, annealing improved the optical qualities. An increase in the below band-gap, green band emission was also observed under some annealing conditions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.