Abstract
ABSTRACTCu(InGa)Se2 films have been deposited by multisource elemental evaporation at substrate temperatures from 550 to 400°C to determine the effect of temperature on grain size and morphology and on solar cell performance. Films were deposited with different flux profiles to compare cases where a copper selenide phase is formed during different stages of growth or not at all. The grain size and surface area of the films are determined by analysis of atomic force microscope images. With the Cu-rich growth, the mean lateral grain area decreases from 1.8 to 0.3 μm2 as substrate temperature decreases. Device efficiency decreases with the lower temperature but cannot be simply attributed to changes in grain size, surface area, or the availability of sodium which diffused from the glass substrate. Instead the decrease in open circuit voltage and fill factor are attributed to a greater density of intra-grain trap states in the Cu(InGa)Se2.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.