Abstract
The effect of grain refinement on the fluidity of AlSi7Mg and AlSi11Mg has been investigated by spiral tests. Two different types of grain refiners have been evaluated. An AlTi5Bl master alloy was added to different Ti contents. Since the commercial alloys had a high initial content of titanium, model alloys were made to investigate the fluidity at low grain refiner additions. Commercial alloys grain refined only by boron additions have also been investigated. The results from the fluidity measurements have been verified by measuring the dendrite coherency point of the different cast alloys. Although different, the two methods show similar trends. The spirals from each fraction grain refiner cast were subsequently investigated metallographically at the tip of the spirals and at a reference point a distance behind, but no obvious difference in structure was observed. For both alloys, an increase in fluidity is observed as the content of grain refiner increases above 0.12 pct Ti, while the fluidity is impaired with increased grain refinement below 0.12 pct Ti. The alloys grain refined with ~0.015 pct B show the highest fraction solid at dendrite coherency, the smallest grain size, and the best fluidity.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.