The influence of liquid penetration at grain boundary regions on the rate of advance of the solid-liquid interface during isothermal solidification of transient liquid phase (TLP) brazed nickel joints has been examined. The test samples used in this study were Ohno-cast nickel with a grain size of >4 mm and a fine-grained nickel with a grain size of around 40 μm. Both Ni-base materials had the same chemical composition. The rate of isothermal solidification was greater when fine-grained nickel was employed during TLP brazing using Ni-11 wt pct P filler metal at 1200 °C. Liquid penetration at grain boundaries accelerates the isothermal solidification process by increasing the effective solid-liquid interfacial area and increasing the rate of solute diffusion into the base material. An analysis of electron channeling patterns has confirmed that random high-angle boundaries have a greater influence on the rate of isothermal solidification than ordered boundaries including small-angle or twin boundaries.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.